# generated using pymatgen
data_Mn2GaCu3
_symmetry_space_group_name_H-M   'P 1'
_cell_length_a   4.86442982
_cell_length_b   4.86442982
_cell_length_c   11.88190439
_cell_angle_alpha   90.00000000
_cell_angle_beta   90.00000000
_cell_angle_gamma   120.00000000
_symmetry_Int_Tables_number   1
_chemical_formula_structural   Mn2GaCu3
_chemical_formula_sum   'Mn6 Ga3 Cu9'
_cell_volume   243.48968586
_cell_formula_units_Z   3
loop_
 _symmetry_equiv_pos_site_id
 _symmetry_equiv_pos_as_xyz
  1  'x, y, z'
loop_
 _atom_site_type_symbol
 _atom_site_label
 _atom_site_symmetry_multiplicity
 _atom_site_fract_x
 _atom_site_fract_y
 _atom_site_fract_z
 _atom_site_occupancy
  Mn  Mn0  1  0.66666700  0.33333300  0.95846400  1
  Mn  Mn1  1  0.66666700  0.33333300  0.70820300  1
  Mn  Mn2  1  0.33333300  0.66666700  0.29179700  1
  Mn  Mn3  1  0.33333300  0.66666700  0.04153600  1
  Mn  Mn4  1  0.00000000  0.00000000  0.62513100  1
  Mn  Mn5  1  0.00000000  0.00000000  0.37486900  1
  Ga  Ga6  1  0.66666700  0.33333300  0.33333300  1
  Ga  Ga7  1  0.33333300  0.66666700  0.66666700  1
  Ga  Ga8  1  0.00000000  0.00000000  0.00000000  1
  Cu  Cu9  1  0.33333300  0.16666700  0.16666700  1
  Cu  Cu10  1  0.83333300  0.16666700  0.16666700  1
  Cu  Cu11  1  0.83333300  0.66666700  0.16666700  1
  Cu  Cu12  1  -0.00000000  0.50000000  0.50000000  1
  Cu  Cu13  1  0.50000000  0.50000000  0.50000000  1
  Cu  Cu14  1  0.50000000  0.00000000  0.50000000  1
  Cu  Cu15  1  0.66666700  0.83333300  0.83333300  1
  Cu  Cu16  1  0.16666700  0.83333300  0.83333300  1
  Cu  Cu17  1  0.16666700  0.33333300  0.83333300  1