# generated using pymatgen
data_CoSi4Ni
_symmetry_space_group_name_H-M   'P 1'
_cell_length_a   3.81339560
_cell_length_b   3.81339560
_cell_length_c   18.67781574
_cell_angle_alpha   90.00000000
_cell_angle_beta   90.00000000
_cell_angle_gamma   120.00000000
_symmetry_Int_Tables_number   1
_chemical_formula_structural   CoSi4Ni
_chemical_formula_sum   'Co3 Si12 Ni3'
_cell_volume   235.22335533
_cell_formula_units_Z   3
loop_
 _symmetry_equiv_pos_site_id
 _symmetry_equiv_pos_as_xyz
  1  'x, y, z'
loop_
 _atom_site_type_symbol
 _atom_site_label
 _atom_site_symmetry_multiplicity
 _atom_site_fract_x
 _atom_site_fract_y
 _atom_site_fract_z
 _atom_site_occupancy
  Co  Co0  1  0.00000000  0.00000000  0.00000000  1
  Co  Co1  1  0.66666700  0.33333300  0.33333300  1
  Co  Co2  1  0.33333300  0.66666700  0.66666700  1
  Si  Si3  1  0.66666700  0.33333300  0.96001600  1
  Si  Si4  1  0.33333300  0.66666700  0.78998400  1
  Si  Si5  1  0.00000000  0.00000000  0.87668300  1
  Si  Si6  1  0.66666700  0.33333300  0.70665100  1
  Si  Si7  1  0.33333300  0.66666700  0.29334900  1
  Si  Si8  1  0.00000000  0.00000000  0.12331700  1
  Si  Si9  1  0.66666700  0.33333300  0.21001600  1
  Si  Si10  1  0.33333300  0.66666700  0.03998400  1
  Si  Si11  1  0.00000000  0.00000000  0.62668200  1
  Si  Si12  1  0.66666700  0.33333300  0.45665000  1
  Si  Si13  1  0.33333300  0.66666700  0.54335000  1
  Si  Si14  1  0.00000000  0.00000000  0.37331800  1
  Ni  Ni15  1  0.66666700  0.33333300  0.83333300  1
  Ni  Ni16  1  0.33333300  0.66666700  0.16666700  1
  Ni  Ni17  1  0.00000000  0.00000000  0.50000000  1